热塑性低烟无卤阻燃聚烯烃系列电缆料系列二
所属分类：
低烟无卤阻燃聚烯烃电缆料以优选树脂做基材，加入优质阻燃剂，润滑剂等其他助剂，经过特殊工艺加工而制得的颗粒料。
产品性能
低烟无卤阻燃聚烯烃电缆料以优选树脂做基材，加入优质阻燃剂，润滑剂等其他助剂，经过特殊工艺加工而制得的颗粒料。
Low-smoke, halogen free and flame retardant polyolefin jacket compound based on superior POE resin, isoroduced and pelletized by special technoloay with addina superior flame retardant. lubricant and othelspecial additives.
产品型号
| 牌号 Type | 名称 Product | 用途 Application |
| KPW-5890DMC |
低摩擦热塑性低烟无卤阻燃聚烯烃电缆料 Anti-friction thermoplastic low-smoke,halogen free and flame retardant polyolefin jacket compound |
低摩擦皮线缆专用 For low-friction cable |
| KPW-5890H |
热塑性低烟无卤阻燃聚烯烃电缆料 Thermoplastic low-smoke, halogen free and flame retardant polyolefin jacket compound |
吊线专用 For drop fiber cable |
加工工艺
推荐的挤出温度如下:
The following temperature profile of extruder is recommended:
|
位置 Zone |
1区 Zone1 |
2区 Zone2 |
3区 Zone3 |
4区 Zone4 |
5区 Zone5 |
机头 Head |
模口 Die |
|
温度℃ Temperature |
135 | 140 | 150 | 160 | 170 | 170 | 170 |
储存与运输
产品采用防潮包装，每袋净重25kg，贮存环境应清洁、干燥通风，贮存时间较长时需进行干燥处理，干燥温度为75℃，干燥时间为3小时。保质期一年。
Product adopts moisture proof packaging; net weight is 25kg; be stored in clean, dry and ventilatedplace, drying treatment is required after long-term storage; drying temperature is 75℃; drying time is 3hours: storage period should be less than 12 months.
性能指标
| 序号 |
项目 Item |
单位
Unit |
典型值 Typical value |
测试方法 Test method |
||
| KPW-5890DMC | KPW-5890H | |||||
| 1 |
密度 Density |
g/cm3 | 1.45 | 1.45 | GB1033 | |
| 2 |
拉伸强度 Tensile Strength |
MPa | 13 | 12 | GB1040 | |
| 3 |
断裂伸长率 Elongation at Break |
% | 160 | 210 | ||
| 4 |
空气热老化性能 Thermal Aging Property |
℃x天 | 110x7 | GB/T2951.7 | ||
| 4.1 |
拉伸强度变化率 Variation on Tensile Strength |
% | -5 | -12 | ||
| 4.2 |
断裂伸长率变化率 Variation on Elongation |
% | -7 | -9 | ||
| 5 |
热变形(90℃x4h) Hot Deformation |
% | 12 | 8 | GB8815 | |
| 6 |
低温脆化温度(-40)失效数 Brittle Temperature at -40℃ |
个 | 0 | 0 | GB5470 | |
| 7 |
20℃时体积电阻率 Volume Resistivity at 20℃ |
Ω.m | 2.1x1012 | 5.2x1012 | GB1410 | |
| 8 |
介电强度 Dielectric Strength |
MV/m | 27 | 28 | GB1408 | |
| 9 |
最大烟密度 Smoke Density |
有焰法 Flaming |
- | 60 | 69 | ASTM E 662 |
|
无焰法 No flaming |
- | 198 | 186 | |||
| 10 |
氧指数 Oxygen Index |
% | 36 | 36 | GB2406 | |
| 11 |
卤酸气体含量 Content of Halogen Acid |
IEC60754-2 | ||||
| 11.1 |
PH值 PH Value |
- | 5.6 | 5.7 | ||
| 11.2 |
电导率 Electrical Conductivity |
μ s/mm | 1.6 | 1.6 | ||
| 12 |
毒性指数 Toxicity Index |
- | 1 | 1.1 | NES 713 | |