湖北科普达光电材料有限公司
热塑性低烟无卤阻燃聚烯烃系列电缆料系列三
所属分类：
该材料具有良好的加工工艺性能、物理机械性能及优异的阻燃性能。它可广泛应用于地铁、机车、舰船、程控机房等场所的电力电缆、控制电缆、光缆、市话电缆、信号电缆及各种数据传输电缆等，特别适用于机械物理性能都要求较高场所。
产品性能
该材料具有良好的加工工艺性能、物理机械性能及优异的阻燃性能。它可广泛应用于地铁、机车、舰船、程控机房等场所的电力电缆、控制电缆、光缆、市话电缆、信号电缆及各种数据传输电缆等，特别适用于机械物理性能都要求较高场所。
The product is low smoke and zero halogen flame retardant polyolefin cable material. it has fine processingtechnique, mechanical properties and excellent flame retardant property. lt is widely used in subway, shipsand warships, program-controlled machine room.
产品型号
| 牌号 Type | 名称 Product | 用途 Application |
| KPW-5892 |
高伸率低烟无卤阻燃聚烯烃电缆料 High elongation low-smoke, halogen free and flame retardant polyolefin jacket compound |
皮线用,大伸率优异的机械物 理性能和良好的挤出工艺性能 Rubber-insulated wire used,excellent mechanical performance and extrusion processing property.
|
| KPW-5892T |
热塑性低烟无卤阻燃聚烯烃电缆料 Thermoplastic low-smoke, halogen free and flame retardant polyolefin jacket compound |
皮线,吊线用,抑烟性能好 Good low-smoke for fiber |
加工工艺
推荐的挤出温度如下:
The following temperature profile of extruder is recommended:
|
位置 Zone |
1区 Zone1 |
2区 Zone2 |
3区 Zone3 |
4区 Zone4 |
5区 Zone5 |
机头 Head |
模口 Die |
|
温度℃ Temperature |
120 | 130 | 145 | 150 | 155 | 160 | 160 |
储存与运输
产品采用防潮包装，每袋净重25kg，贮存环境应清洁、干燥通风，贮存时间较长时需进行干燥处理，干燥温度为75℃，干燥时间为3小时。保质期一年。
Product adopts moisture proof packaging; net weight is 25kg; be stored in clean, dry and ventilatedplace, drying treatment is required after long-term storage; drying temperature is 75℃; drying time is 3hours: storage period should be less than 12 months.
性能指标
| 序号 |
项目 Item |
单位 Unit |
典型值 Typical value |
测试方法 Test method |
||
| KPW-5892 | KPW-5892T | |||||
| 1 |
密度 Density |
g/cm3 | 1.43 | 1.46 | GB1033 | |
| 2 |
拉伸强度 Tensile Strength |
MPa | 11 | 12 | GB1040 | |
| 3 |
断裂伸长率 Elongation at Break |
% | 320 | 350 | ||
| 4 |
空气热老化性能 Thermal Aging Property |
℃x天 | 110x240 | GB/T2951.7 | ||
| 4.1 |
拉伸强度变化率 Variation on Tensile Strength |
% | -8 | 3 | ||
| 4.2 |
断裂伸长率变化率 Variation on Elongation |
% | -14 | -18 | ||
| 5 |
热变形(90℃x4h) Hot Deformation |
% | 19 | 17 | GB8815 | |
| 6 |
低温脆化温度(-40)失效数 Brittle Temperature at-40℃ |
个 | 0 | 0 | GB5470 | |
| 7 |
20℃时体积电阻率 Volume Resistivity at 20℃ |
Ω.m | 3.7x1012 | 2x1012 | GB1410 | |
| 8 |
介电强度 Dielectric Strength |
MV/m | 27 | 27 | GB1408 | |
| 9 |
最大烟密度 Smoke Density |
有焰法 Flaming |
- | 92 | 89 | ASTM E 662 |
|
无焰法 No flaming |
- | 210 | 185 | |||
| 10 |
氧指数 Oxygen Index |
% | 34 | 36 | GB2406 | |
| 11 |
卤酸气体含量 Content of Halogen Acid |
IEC60754-2 | ||||
| 11.1 |
PH值 PH Value |
- | 5.5 | 5.6 | ||
| 11.2 |
电导率 Electrical Conductivity |
μ s/mm | 2 | 1.2 | ||
| 12 |
毒性指数 Toxicity Index |
- | 1 | 1 | NES 713 | |