湖北科普达光电材料有限公司
聚乙烯电缆料系列一
所属分类：
该产品具有产品质量稳定，加工工艺性能优越，加工温度范围宽，制品表面光滑细腻，能替代进口及石化同型号产品且具有价格优势。
产品性能
该产品具有产品质量稳定，加工工艺性能优越，加工温度范围宽，制品表面光滑细腻，能替代进口及石化同型号产品且具有价格优势。
The product has features of stable quality, excellent processing technique, wide processing temperature.
产品型号
| 牌号 Type | 名称 Product | 用途 Application |
| KPM0801-1 |
黑色中密度聚乙烯护套料 Black MDPE compound |
光电缆护套 Wire&Cable Jacket |
| KPM0801-II |
黑色中密度聚乙烯护套料 Black MDPE compound |
光电缆护套 Wire&Cable Jacket |
| KPM0801-III |
黑色中密度聚乙烯护套料 Black MDPE compound |
光电缆护套 Wire&Cable Jacket |
| KPH-0802 |
黑色高密度聚乙烯护套料 Black HDPE compound |
光电缆护套 Wire&Cable Jacket |
| KPH0802-1 |
黑色高密度聚乙烯护套料 Black HDPE compound |
光电缆护套 Wire&Cable Jacket |
| KPL-0803 |
黑色线性低密度聚乙烯护套料 Black LLDPE compound |
光电缆护套 Wire&Cable Jacket |
加工工艺
推荐的挤出温度如下:
The following temperature profile of extruder is recommended:
|
位置 Zone |
1区 Zone1 |
2区 Zone2 |
3区 Zone3 |
4区 Zone4 |
5区 Zone5 |
机头 Head |
模口 Die |
|
|
温度℃ Temperature |
MDPE | 160 | 180 | 220 | 235 | 235 | 230 | 230 |
| HDPE | 160 | 190 | 220 | 235 | 235 | 235 | 235 | |
| LLDPE | 140 | 160 | 200 | 220 | 220 | 210 | 210 | |
储存与运输
包装:有750kg、500kg聚乙烯内袋外编织袋大包装，或25kg纸塑复合小包装运输:该产品运输时不得在阳光下暴晒，不得淋雨或受潮，并保持包装完整。
储存:产品储存在清洁、阴凉、干燥通风、远离火源的仓库内，如果发现产品受潮，应在60-80℃的条件下干燥1-2小时后使用。
Packaging: 750kg, 500kg polyethylene inner bag with outer woven bag; or 25kg paper-plastic lamina-tion bag
Transportation: avoid sunshine, rainfall and moistureStorage: Please store in clean, cool, dry and ventilated warehouse; keep away from fire sources; if it wasaffected with damp, please dry under 60-80'℃ for 1 to 2 hours.
性能指标
|
性能 Property |
单位 Unit |
典型值 Typical value | |||||
|
KPM 0801-1 |
KPM 0801-1l |
KPM 0801-IlI |
KPH- 0802 |
KPH 0802-1 |
KPL- 0803 |
||
|
密度 Density |
g/cm3 | 0.942 | 0.951 | 0.960 | 0.960 | 0.955 | 0.940 |
|
熔融指数(190℃) Melting Index |
g/10min | 0.7 | 0.7 | 0.7 | 0.5 | 0.5 | 0.9 |
|
抗张强度 Tensile Strength |
MPa | 21 | 19 | 17 | 22 | 23 | 19 |
|
断裂伸长率 Elongation at break |
% | 750 | 750 | 750 | 850 | 880 | 800 |
|
低温冲击脆化温度 (-76℃) Brittle temperature |
- | PASS | PASS | PASS | PASS | PASS | PASS |
|
耐环境应力开裂 ESCR |
H | 500 | 500 | 96 | 500 | 1000 | 1000 |
|
炭黑含量 Carbon black content |
% | 2.60 | 2.60 | 2.60 | 2.60 | 2.60 | 2.60 |
|
炭黑分散度 Dispersity of carbon black |
级 | 2.5 | 2.5 | 3 | 2.5 | 2.5 | 2.5 |
|
200℃氧化诱导期 OIT |
Min | 45 | 40 | 30 | 45 | 45 | 45 |
|
介电强度 Dielectric strength |
KV/m | 26 | 26 | 25 | 26 | 26 | 26 |
|
20℃体积电阻 Volume resistivity at 20℃ |
Ω.m | 2.5x1014 | 2.7x1014 | 3.2x1014 | 2.3x1014 | 4.5x1014 | 2.5x1014 |
|
介电常数 Dielectric constant |
- | 2.3 | 2.2 | 2.5 | 2.3 | 2.3 | 2.3 |